Q460C carbon and low alloy steel application

Q460C carbon and low alloy steel application

Posted:2015-11-30 13:56:29

Q460C Pressure Vessel Steel Application

 

Q460C hot rolled steel plate, in which Q represents the yield strength, yield strength value of 460 MPa, tensile strength shall be above 550 Mpa, charpy V-notch impacting test shall be done at 0 centigrade.

 

Q460C Chemical Composition:

C

Si

Mn

P

S

V

Nb

Ti

Al (min.)

Cr

Ni

0.20

0.55

1.00-1.70

0.035

0.035

0.02-0.20

0.015-0.060

0.02-0.20

0.015

0.70

0.70

 

Q460C Mechanical Property:

Grade

Mechanical Property

Tensile Strength(MPa)

Yield Strength(MPa)

% Elongation in 2 in.(50mm) min

Impacting Test Temperature(°C)

GB/T1591 Q460C

650-720

460

17

0

 

Q460C Delivery Time or Lead Time: 15-30days

 

Q460C Specification:
Width: 1500-3000mm
Length: 4020-18800mm;
Thickness: 6-700mm

 

Q460C Application:
GB/T1591 Q460C Steel Plate are used in Construction of Bridges, Highway Construction and Other Engineering construction. Because of the hot rolled steel products with high strength, good toughness, easy to processing molding and good weld ability and other excellent properties, then it is widely used in ship, automobile, Bridges, buildings, machinery, pressure vessels and other manufacturing industries.

 

Phone: 0086-18317160019
TEL: 0086-21-61182423
Fax: 0086-21-61182425
E-mail:
 info@katalor.com
Skype: shanghai.katalor
Address : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong
 New District,Shanghai

HOME | ABOUT US | PRODUCT | NEWS | CONTACT US | katalor
Copyright © 2014 by Shanghai Katalor Enterprises Co., Ltd All rights reserved