SUS316L SUS series of stainless steel in Japan, has a very good resistance to crystal corrosion and oxidation resistance, strength, easy processing, no need for annealing after welding. For pulp and paper industry, marine and shipbuilding industry and other industries and civilian areas.
|
Grade |
|
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
N |
|
316L |
Min |
- |
- |
- |
- |
- |
16.0 |
2.00 |
10.0 |
- |
|
Max |
0.03 |
2.0 |
0.75 |
0.045 |
0.03 |
18.0 |
3.00 |
14.0 |
0.1 |
SUS316L Physical Properties：
Grade |
Density |
Elastic Modulus |
Mean Co-eff of Thermal Expansion (µm/m/°C) |
Thermal Conductivity |
Specific Heat 0-100°C |
Elec Resistivity |
|||
|
0-100°C |
0-315°C |
0-538°C |
At 100°C |
At 500°C |
|||||
|
316L |
8000 |
193 |
15.9 |
16.2 |
17.5 |
16.3 |
21.5 |
500 |
740 |
SUS316L process performance：
316L stainless steel has good cold and hot processing performance, good thermoplasticity of steel, overheating sensitivity is low, the appropriate heat processing temperature of 900 ~ 1000 ℃. As the Mo-containing steel is higher, the deformation resistance than the 304 and 304L significantly higher.Cold processing performance is good, can be cold-rolled, cold drawn, deep drawing bending, curling folding cold and cold forming.
Solution temperature is 1050 ~ 1100 ℃, cooling method: water cooling or air cooling, according to the product section size.
Welding: In order to maintain good resistance to intergranular corrosion, after solution treatment should be carried out, if not allowed to heat treatment, to use 316L.
Phone: 0086-18317160019
TEL: 0086-21-61182423
Fax: 0086-21-61182425
E-mail: info@katalor.com
Skype: shanghai.katalor
Address : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai