ASTM 1008 steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.
ASTM1008 steel applications ASTM1008 steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.
ASTM 1008 chemical composition:
Grade |
C % | Si % | Mn % | P % | S % |
| ASTM 1008 | 0.10 | - | 0.30-0.50 | 0.040 | 0.050 |
ASTM 1008 steel Mechanical Properties
| ASTM 1008 Properties | Metric | Imperial |
| Tensile strength | 340 MPa | 49300 psi |
| Yield strength (depending on temper) | 285 MPa | 41300 psi |
| Elastic modulus | 190-210 Gpa | 27557-30458 ksi |
| Bulk modulus (typical for steel) | 200 GPa | 29000 ksi |
| Shear modulus (typical for steel) | 80.0 GPa | 11600 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 20% | 20% |
| Reduction of area | 45% | 45% |
| Hardness, Brinell | 95 | 95 |
| Hardness, Knoop (converted from Brinell hardness) | 113 | 113 |
| Hardness, Rockwell B (converted from Brinell hardness) | 55 | 55 |
| Hardness, Vickers (converted from Brinell hardness) | 98 | 98 |
| Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing) | 55 | 55 |
Katalor enterprises is the ASTM 1008 steel supplier,we provide various type of ASTM 1008 steel,also provide ASTM 1008 steel deep processing,if you need ASTM 1008 steel machine processing,and ASTM 1008 steel,contact us!